Silicon Nanowires in Lithium Batteries

A couple of months ago, I wrote a post about a promising development in using Sodium in the chemistry for FePO4F cathode cells. Now I have a promising development to report on anode materials.

In an advance on-line letter to Nature Nanotechnology, Chan et al., report on the use of silicon nanowires in the place of the more common carbon graphite anode material ("High-performance lithium battery anodes using silicon nanowires", Nat. Nano. (advanced online) 16 December, 2007).

Silicon is, theoretically, a superior material for the anode compared to carbon. The theoretical charge capacity for a lithium-silicon battery is around 4.2 Ah g-1 compared to 0.37 Ah g-1 for graphite-based anodes. In the experiment, they achieved stable performance around 3.1-2.1 Ah g-1 for the output. Just by way of comparison, if one could achieve a cell voltage of 3.5 V and 2.5 Ah g-1 charge capacity, that corresponds to 8.75 kWh/kg or 31.5 MJ/kg (of anode material only -- the remainder of the battery might constitute +75 % of the mass). Gasoline (iso-octane) contains 44.4 MJ/kg and only about 30 % of that is actually used as work in spinning the wheels. So this is a potentially very significant result. When you take into account the greater mass of an internal combustion engine compared to an electrical motor, the electrical car has potentially a higher energy density.

However, silicon suffers from a massive volume change when transforming from lithium loaded to unloaded -- about 400 %. In comparison, the previous article on a sodium-ion cathode material reported an improvement in volume change to 3.7 % from 6.7 %! Obviously, these are not even remotely in the same regime, aside from the fact that one is an anode and the other the cathode. As I explained previously, the volume change is often a good indicator as to the resilience of a battery over tens of thousands of cycles. A 6.7 % can be accommodated by a crystal lattice without major movement of individual atoms. A 400 % volume change implies massive bond breaking and reconfiguration. There is no way a crystalline material can withstand such changes so any silicon anode must be amorphous.

The advance reported by Chan et al. is to form the silicon into a 'forest' of small diameter (~100 nm or several hundred atoms across) nanowires. Nanowires are, in general, better able to handle large changes in dimension due to thermal expansion, etc., because they can elongate freely without breaking up. Nanowires may also accommodate stress by curling up, like a spring. If a bulk material tried to expand that much, it would run into the material to its right and left, they would have a violent disagreement as things often do when they run out of space, and everything would (literally) fall apart.

From a manufacturing perspective, it is fairly straight-forward to fabricate such a 'forest' of nanowires. A typical method would be to anneal a thin film of Silicon Sub-oxide (i.e. SiOx, where x < 2) in a thin atmosphere of Silane gas (SiH4) that has some small catalyst (Fe/Ni) particles embedded in it. In this case, they used gold nanoparticles on a nickel substrate. The catalysts absorb silicon from the gas and grow outwards, forming nanowires.

The nanowires Chan et al. grew were initially crystalline but they found via electron microscopy that they quickly became amorphous after cycling. This phase change was accompanied by a significant loss of performance. The charge capacity was found to be 4.277 Ah g-1 after the first cycle to 3.541 Ah g-1 for the second. The efficiency of the cells was only 72 % for the first cycle but rose to 90 % after that, which is typical for lithium cells (i.e. multiply the given charge capacity by the efficiency to get the charge they got out of the cells). The author's report that, "The mechanism of the initial irreversible capacity is not yet understood and requires further investigation." I don't think it's a stretch to infer that the phase change from crystalline to amorphous is the reason. One would likely achieve better results by starting with amorphous silicon nanowires and not putting the system through that initial shock.

On the negative side, the volume change is still immense. I'm unsure that these structures can hold up over tens of thousands of cycles like other chemistries can. The report only conducted 10-20 cycles. While the graphs shown in the paper the suggest the performance becomes asymptotic (stabilizes) at 20 cycles, that likely is due to the phase change from crystalline to amorphous being fully completed. There could well be some 'cliff' out around several hundred cycles where the wires embrittle and begin to break.

Update: edited to fix a broken tag that ate a chunk of the post. Silly blogger editor.


Anonymous said...

Wow Robert, I found your sodium ion post the other day and was impressed by that one, but this one could be really incredible.

I'm no expert but it would seem to me that a battery with sodium-silicon chemistry would be just about ideal from a cost/resource standpoint. Both plentiful and cheap. Again, wow!

One other thing, isn't silicon less reactive than carbon? Wouldn't this sort of chemistry be safer too?

Robert McLeod said...

They are both important results in their own fashion. I would expect it will take a number of years for each advance to find itself into production batteries. Integrating the two of them will take even more time.

One other factor that I didn't discuss is how physically tough they will be. These are basically cantilevered beams so they can break if you pass a shock wave through them (by say, dropping). I would be interested if they have determined the bulk density of this material, since the buoyancy of the electrolyte is important to guess how resistant they will be to shock damage.

On the safety front, since they are storing more energy in a smaller area, I doubt they would be any safer. I think the safety issue with lithium batteries is overblown anyway -- it's mostly a quality control problem with counterfeit cells.

Anonymous said...

This is a great demostration. If it works, the possibility is endless.
For the small portable battery application, I still see a physical challenge for the apporach. Using Si nano-wire, it still swelling. 4 time of its size. Inside a portable battery, the space is confined and filled with hard(liquid) materials. The challenge is to design this battery structure to accomodate the volume change during charge cycle.
Robert, do you have any number we can use to estimate the significant of the volume change for a typical cell phone battery using Si-Nano-wire anode?

Robert McLeod said...

I'm afraid I have no real idea what proportion of the volume in a battery the anode typically takes up. You would have to take some apart to make a guess at it.

Rik said...

I read about this a week or so ago, I'm not sure where (maybe on Nature itself indeed). I wouldn't say that the volume change in nanowire would be a problem perse. Mechnanics on such a small scale are very different from what we are used to on a larger scale.

Anonymous said...

In most commercial Li ion batteries today, the positive and negative electrodes occupy about 55% and 35% of the solid volume. So even if the volume of the negative electrode is reduced to nearly zero by using Si nanowire, the capacity of the battery will increase by a factor of about 1.8, not 10 as claimed by some sources.

Unknown said...

Hi Robert,
Usually I do not read article on blogs, but I would like to say that this write-up very pressured me to check out and do it! Your writing taste has been surprised me. Thank you, quite nice article.

Merlen Hogg